| Porcelain Fused To Metal | |||||||
| ARGEDENT 75 | ARGEDENT BIO 862PF | ARGEDENT EURO | ARGELITE 61 | NOBELCROWN NF | REMANIUM 2001 | SUPERBOND | |
|---|---|---|---|---|---|---|---|
| CLASSIFICATION | High Gold High Noble Alloy | High Gold High Noble Alloy | Reduced-Gold High Noble Alloy | Palladium-Silver Noble Alloy | Palladium-Co – CR Noble Alloy | Base – Nickel Free | Non-Precious Predominantly Base Alloy |
| Technical Data | |||||||
| COLOR | Yellow | Yellow | White | White | White | White | White |
| DENSITY (G/CM3) | 16.2 | 18.6 | 12.8 | 11.2 | 9.2 | 8.6 | 8.3 |
| MELTING RANGE (°F – °C) | 2145 – 2200 (°F) | 1040 – 1160 (°C) | 2050 – 2300 (°F) | 2066 – 2327 (°F) | 2280 – 2350 (°F) | 1325 (°C) | 1301 – 1364 (°C) |
| CASTING TEMP. (°F – °C) | 2355 (°F) | 1280 (°C) | 2550 (°F) | 2498 (°F) | 2550 (°F) | 1415 (°F) | |
| CTE 25 °C – 500 °C | 14.4 | 14.4 | 14.1 | 14.5 | 14.4 | 14.2 | 14.7 |
| CTE 20 °C – 600 °C | 14.7 | 14.6 | 14.4 | 14.7 | 14.7 | – | – |
| ELONGATION (%) | 8.0 | 10.0 | 9.0 | 13.0 | 13.0 | 5.5 | 3.0 |
| VICKERS HARDNESS | 240 | 220 | 290 | 310 | 310 | 336 | 200 |
| 0.2 % PROOF STRESS (MPA) | – | – | – | – | 660 | 316 | |
| Composition In % | |||||||
| Au 75.1 | Au 86.2 | Au 40.0 | Au 0.0 | Au 0.0 | Co 63.0 | Ni 61.0 | |
| Pt 12.0 | Pt 11/5 | Pd 39.4 | Pd 60.5 | Pd 25.0 | Cr 23.0 | Cr 25.0 | |
| Ag 10.0 | Pd 0.0 | Ag 10.0 | Ag 28.1 | Ag 0.0 | Mo 7.3 | Mo 10.5 | |
| In 1.8 | Ag 0.0 | In 8.8 | Sn 2.5 | Co 42.75 | W 4.3 | Si 1.5 | |
| Sn 1.00 | Zn 1.5 | Ga 1.4 | In 6.6 | Cr 20.0 | Si 1.6 | Ti <1.0 | |
| Ir <1.0 | Ru,Mn <1.0 | Sn <1.0 | Ga 2.1 | Mo 12.0 | Mn <1.0 | Fe <1.0 | |
| Ta <1.0 | Ru <1.0 | Ru <1.0 | B <1.0 | Al, Co <1.0 | |||
| For Full Cast Crown | |||||||
| ARGENCO 75 | ARGENCO 58 | ARGENCO 40 | ARGENCO Y+ | ARGENCO W+ | |||
|---|---|---|---|---|---|---|---|
| CLASSIFICATION | High Noble | High Noble | Noble | Noble | Noble | ||
| Technical Data | |||||||
| TYPE | 3 | 3 | 3 | 3 | 3 | ||
| COLOR | Yellow | Yellow | Yellow | Yellow | White | ||
| DENSITY (G/CM3) | 15.5 | 13.9 | 12.4 | 10.5 | 10.5 | ||
| MELTING RANGE (°F) | 1710 – 1760 | 1681 – 1770 | 1571 – 1697 | 1904 – 2048 | 1850 – 2000 | ||
| CASTING TEMP. (°F) | 1900 | 1905 | 1850 | 2210 | 2145 | ||
| ELONGATION (%) | 19.0 | 10.0 | 30.0 | 5.0 – 6.0 | 9.0 | ||
| VICKERS HARDNESS | 182 | 210 | 125 | 180 | 180 | ||
| 0.2 % PROOF STRESS (MPA) | – | – | – | – | – | ||
| Composition In % | |||||||
| AU | 74.5 | 58.0 | 40.0 | 2.0 | 2.0 | ||
| PD | 3.5 | 3.25 | 4.95 | 34.9 | 24.9 | ||
| AG | 11.0 | 27.0 | 45.7 | 30.0 | 68.0 | ||
| CU | 10.5 | 10.5 | 8.3 | 0.0 | 0.0 | ||
| ZN | < 1.0 | 1.0 | 1.0 | 3.0 | 2.0 | ||
| IN | – | < 1.0 | – | 30.0 | 3.0 | ||
| IR | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 1.0 | ||
| B | – | – | – | < 1.0 | – | ||